Pixel Filament ASA - Singularity Reusable Spool - 1kg
Click to open expanded view

Pixel Filament ASA - Singularity Reusable Spool - 1kg

Stock held in New Zealand unless stated for Pre order

1 review
Price
$34.00
Tax included. Shipping calculated at checkout.
Compare colours via the HEX CODE in the Polymaker APP below

Color: Black 1.75mm

Weight: 1kg

SKU: PIX-ASA-SINGULARITY-SP

Pixel Filament ASA - Singularity Reusable Spool - 1kg

SKU
Color
Weight
Price
Pixel Filament ASA - Singularity Reusable Spool - 1kg
PIX-ASA-SINGULARITY-SP Black 1.75mm 1kg
$34.00
Compare product options
20 in stock and ready for shipping

Pickup available at Formtech Auckland

Usually ready in 1 hour

Check availability at other stores
Apple Pay
Google Pay
Mastercard
Shop Pay
Visa
  • What it is: Affordable, high‑grade 1.75 mm 3D printing filament made from polymers sourced from qualified suppliers.
  • Proven quality: Selected after extensive supplier qualification, testing, and community feedback to match or exceed major brands for reliability and print accuracy.
  • Compatibility and performance: Consistent extrusion, strong layer adhesion, and smooth finished surfaces across common materials like PLA, PETG, and TPU.

Why Pixel Filament?

Pixel Filament is an affordable and dependable 3D printing filament made from high grade polymers sourced from qualified, proven suppliers. After testing numerous manufacturers, we selected partners that consistently delivered accuracy, reliability, and print quality equal to or better than major global brands.

Pixel Filament was created to give makers an option that delivers excellent results without inflated costs. Years of print testing, community feedback, and hands-on evaluation of multiple filament sources led us to a product we are proud to stand behind.

Physical and Mechanical Properties

Category Subject Testing Method Data
Physical Density ISO 1183 1.05 g/cm3
Melt Index 260°C, 2.16 kg 7.0 ± 0.8 g/10 min
Melting Temperature DSC, 10°C/min 210 °C
Glass Transition Temperature DSC, 10°C/min N/A
Crystallization Temperature DSC, 10°C/min N/A
Vicat Softening Temperature ISO 306; GB/T 1633 106 °C
Heat Deflection Temperature ISO 75 1.8 MPa 92 °C
Saturated Water Absorption Rate 25°C, 55% RH 0.45%
Mechanical Young's Modulus (X-Y) ISO 527; GB/T 1040 2450 ± 270 MPa
Young's Modulus (Z) ISO 527; GB/T 1040 2120 ± 260 MPa
Tensile Strength (X-Y) ISO 527; GB/T 1040 37 ± 3 MPa
Tensile Strength (Z) ISO 527; GB/T 1040 31 ± 4 MPa
Breaking Elongation Rate (X-Y) ISO 527; GB/T 1040 9.2 ± 1.4 %
Breaking Elongation Rate (Z) ISO 527; GB/T 1040 4.6 ± 0.8 %
Bending Modulus (X-Y) ISO 178; GB/T 9341 1920 ± 130 MPa
Bending Modulus (Z) ISO 178; GB/T 9341 1650 ± 120 MPa
Bending Strength (X-Y) ISO 178; GB/T 9341 65 ± 5 MPa
Bending Strength (Z) ISO 178; GB/T 9341 40 ± 3 MPa
Impact Strength (X-Y) ISO 179; GB/T 1043 41.0 ± 2.3 kJ/m2; 19.6 ± 1.8 kJ/m2 (notched)
Impact Strength (Z) ISO 179; GB/T 1043 4.9 ± 0.6 kJ/m2

 

Recommended Print Settings

Parameter Value
Nozzle Temperature 240–270 (°C)
Drying Settings before Printing Blast Drying Oven: 80 °C, 8 h
Printing and Storage Humidity < 20% RH (Sealed; with desiccant)
Nozzle Size 0.2 mm; 0.4 mm; 0.6 mm; 0.8 mm
Base Plate Temperature 80–100 (°C)
Build Plate Type Engineering Plate; High Temperature Plate; Textured PEI Plate
Cooling Fan 0–80%
Printing speed < 250 mm/s
Retraction speed 20–40 mm/s
Chamber Temperature 45–60 °C
Max Overhang Angle ~ 70°
Max Bridging Length ~ 40 mm

 